Abstract
O objetivo principal deste estudo, foi realizar uma revisão integrativa sobre a distribuição das partículas do biomaterial de enxerto após mistura com plasma rico em plaquetas (PRF). As seguintes palavras-chave foram aplicadas: (platelet rich fibrin) OR (PRF); AND (block) OR (bone graft); AND (CBCT) OR (micro-CT) OR (microscopy), entre Fevereiro e Maio de 2021. Os critérios de inclusão envolveram, ensaios clínicos randomizados controlados, estudos pré-clínicos randomizados, estudos prospetivos, relatos de caso, um estudo de caso - coorte única, um estudo comparativo e um estudo em animais.
Análises obtidas por micro-CT revelaram uma homogeneidade na distribuição de partículas no bloco de L-PRF e revelou um volume médio de 37,7% ± 1,7% para as partículas de DBBM no bloco de L-PRF. A distância média entre as partículas DBBM foi de aproximadamente
60.55 µm (0.0605 mm) na imagem A, e de 226.3 µm (0.23 mm) na imagem B, que foi visualizada nas imagens de SEM (microscopia eletrónica de varredura).
Este estudo é inconclusivo, são necessárias medições e avaliações em meio laboratorial através de microscopia eletrónica, uma vez que as imagens onde se realizaram estas avaliações são insuficientes para validar a veracidade e representatividade destas medidas. The main aim of this study was to perform an integrative review on the distribution of inorganic graft material particles within the platelet rich fibrin (PRF) block. The following keywords were applied: (platelet rich fibrin) OR (PRF); AND (block) OR (bone graft); AND (CBCT) OR (micro-CT) OR (microscopy), between February and May 2021. Inclusion criteria involved randomized controlled clinical trials, randomized preclinical studies, prospective studies, case reports, a case study - single cohort, a comparative study and a animal study. Micro-CT analyses revealed that the particles were homogenously distributed within the L-PRF block, without contact with each other and revealed a mean volume of 37.7% ± 1.7% for the DBBM particles in the L-PRF block. However, no measurement was performed torecord. The distance between the DBBM particles was approximately 60.55 µm (0.0605 mm) in image A, and 226.3 µm (0.23 mm) in image B, which was visualized in the images by SEM (Scanning electron microscopy).
This study is inconclusive, measurements and evaluations in the laboratory through electron microscopy are necessary, since the images where these evaluations were carried out are insufficient to validate the veracity of these measurements.